FS4050HT – UCC Petrolatum Tape HT (High Temperature) 50mm X 10M UCC Petrolatum Tape HT UCC Petrolatum Tape HT is composed of a non-woven synthetic fabric carrier fully impregnated with a neutral petrolatum compound stabilised with inert fillers and complemented with corrosion inhibitors. For operating temperatures up to 75°C. UCC Petrolatum Tape HT is deigned to provide long term corrosion protection to pipes flanges valves and other fittings. Features Surface Tolerance on marginally prepared substrates; St 2.0. Conforms to irregular shapes and profiles. Can be applied to cold wet substrates. Unaffected by water acid salts or bacterial attack. Encapsulates lead painted substrates. Nil VOC s. Ease of application at high and low temperature extremes. Ready for immediate service no curing time. Conforms with AWWA C 217-04. Application Prepare surface to St 2 std. Apply UCC Petrolatum Primer to substrate at a spread rate of 3kg/m² approx. Profile projections and voids with UCC Petrolatum Mastic. Spirally apply tape incorporating 55% overlap to achieve a double thickness with circumferential turn. Overwrap tape with UCC PVC OverWrap spirally applied with 55% overlap. Product Properties: Properties | Test Method | Value Thickness | ASTM D1000 | 1.1mm to 1.5mm Weight | 1.44kg/m² | 1.44kg/m² Breaking Strength | ASTM D1000 | 6.0 N/mm Elongation at Break | ASTM D1000 | 15% Breakdown Voltage (2 layers) | ASTM D149 | >16kv Water Vapour Transmission Rate | ASTM E96 | 0.25g/m² /24hr Cathodic Disbondment | ASTM G8 | <700mm² Application Temperature: -10 to +55ºC Service Temperature: -20 to +75ºC Excursion Peak Temperature: 80ºC